Conveyor belt repair strip bonding

It is mainly used for the repair of longitudinal long-distance scratches, scratches and edge wear of the conveyor belt, and the repair of local rubber layer damage.

Conveyor belt repair strip bonding

Sep 23,2020

Hot-melt rubber repair agent technology

1. Turn on the heating switch of the preheating glue gun 20 minutes in advance to preheat to the set temperature. 2. Grinding the broken rubber surface of the conveyor belt with a tungsten steel grinding disc. Pay attention to prevent polishing or scorching during grinding. 3. Cleaning and activation shall be fully mixed according to LPT920 treatment agent A and B, and LPT920 treatment agent shall be evenly coated on the treated rubber surface. Temperature 25 ℃, humidity 60%, air for 10 minutes, when the temperature is low, should extend the drying time or hot air gun dry. (Treatment agent is now prepared and used)

Hot-melt rubber repair agent technology

Sep 23,2020

Backing filling material operation process

1. Clean and prepare to remove the residual filler on the cone surface, oil stains and dirt on the parts in contact with the glue; Mount the cone and liner; Seal the cone/liner mating surface and ring hole with adhesive tape to prevent glue leakage and protect the thread on the shaft if necessary; When using, try to construct at 5-30 ℃. 2. Fix the stirrer on the low-speed hand electric drill with glue, and open LPT880 backing filling material component A, stir for 1 minute, then pour component B into component A barrel and stir with an electric stirrer. The color is uniform. Generally, the stirring time is not more than 4 minutes. 3. Pouring the mixed LPT880 glue solution and injecting it along a gap between the cone or lining plate to facilitate exhaust. If necessary, plasticine and the like can be used as cofferdam guide until it overflows from the top of the gap. Do not inject glue that is not evenly mixed (different color).

Backing filling material operation process

Sep 23,2020

Cold vulcanization roller coating operation process

Cold vulcanization roller encapsulation is used in conjunction with LPT3000, ER-45, LPT330 and LPT918. Operation process: Grind the roller and rubber plate to clean up the residual rubber and other impurities on the roller, and then use a grinding machine to grind out a rough surface without rust points on the roller; Roughening and roughening the sticky surface of the rubber plate (if there is a semi-vulcanized layer, only need to be cleaned).

Cold vulcanization roller coating operation process

Sep 23,2020

Repair Technology of Large Area Damage of Conveyor Belt

Repair with LPT919 high strength repair agent. Grinding and cleaning: clean the worn surface of the conveyor belt, polish the grinding disc with tungsten steel and clean it with LPT360 cleaning agent. Coating primer: brush the rubber primer on the treated wear surface and dry it naturally or by heating. Scraping glue: pour the prepared LPT919 repair agent immediately and evenly onto the treated rubber surface, and quickly scrape the glue with a short brush or scraper.

Repair Technology of Large Area Damage of Conveyor Belt

Sep 23,2020

Wear-resistant coating operation process

1. The surface treatment of the base material shall be roughened to the construction part, clean and dry. 2. According to the mass ratio of LPT228 large particles 3:1,LPT226 small particles 4:1. Accurately mix the and B components evenly and use them up within 30 minutes, that is, use them to cure without glue and cause waste. 3. Scraping wear-resistant coating The mixed material is coated layer by layer on the part to be constructed. After being coated to a suitable thickness, the surface shall be treated smoothly. When scraping, the coating shall be compacted to fully soak with the substrate. The thickness of wear-resistant coating should be 4-8mm, and the maximum thickness can be 30mm. 4, curing 25 ℃ curing 24 hours, can be put into use. When the temperature is low, heat should be applied or the curing time should be extended. After the coating is cured for 24 hours, it can be heated from 60 ℃ to 80 ℃ for 2 hours to obtain better comprehensive performance.

Wear-resistant coating operation process

Sep 23,2020

Conveyor belt joint fabrication and cold vulcanization bonding

The normal temperature fast bonding of the conveyor belt joint is to use the normal temperature curing adhesive to bond the conveyor belt joint. Bonding without heating and pressure curing, no special equipment and tools, simple process, short operation time, low labor intensity, low cost, easy control of bonding quality, good bending resistance of bonding joints, no special requirements for the environment, the bonded joints can be put into use in a short time, suitable for the bonding of layer core conveyor belt joints in various environments.

Conveyor belt joint fabrication and cold vulcanization bonding

Sep 23,2020

Thermal Vulcanization Process of Conveyor Belt

Vulcanization Process of (I) Layer Core Conveyor Belt 1. Surface Treatment: The conveyor belt joint is made into an oblique stepped cover joint according to the lap length of 1/2 bandwidth, then the surface of the joint is rouged, cleaned, decontaminated and dried with cleaning agent. 2. Mastic coating: evenly coat the surface of the joint and the vulcanized film with the vulcanized rubber paste for one or two times. After the solution volatilizes until the rubber surface is basically dry, the vulcanized film is pasted on the surface of the joint coated with the vulcanized rubber paste, and a buffer rubber strip is pasted at the gap of the same cloth layer (note that if the glue is not applied thoroughly, bubbles will be generated, resulting in reduced bonding performance). 3. Laying and pressurizing: After the glue solvent volatilizes until the glue surface is basically dry, divide the two

Thermal Vulcanization Process of Conveyor Belt
< 1 >

SAF Coolest v1.3.1.1 设置面板BQOSX-AUGS-DAAEE-ZZE

图片ALT信息： Hubei HuangshiDe New Material Technology Co., Ltd.
违禁词： First, best, first-class, leading, unique, king, leader, leader, extreme,
营业执照及SEO链接： Business License

无数据提示

Sorry, the current column is being updated, please look forward to it!

You can view other columns or returnHome Page

V1.3.1 SVG图标库请自行添加图标，用div包起来，并命名使用